Meraki Star Metals Oil & Gas Equipment Trading L.L.C. titanium grade 12 pipes are generally enjoyed due to their high strength, extraordinary assurance from split disintegration and pitting, weight saving possibilities, incredible weldability, and usefulness. It is similarly used due to being a bewildering assurance from the erosive and horrendous action of higher temperature destructive steam. It is having more vital ability to persevere through cool/wet and dry/hot destructive gas stacking. It is sensible laying and twisting onto the seabed. It is having a part of being low modulus, weariness resistance, and more unmistakable break strength. This grade pipe is similarly assurance from utilization depletion and stress disintegration breaking.

Titanium Gr 12 Pipes & Tubes Manufacturers, Titanium Gr 12 Pipes & Tubes Suppliers, Titanium Gr 12 Pipes & Tubes Stcokists, Titanium Gr 12 Pipes & Tubes Exporters

Titanium Gr 12 Pipes & Tubes Manufacturers in UAE, Titanium Gr 12 Pipes & Tubes Suppliers in UAE, Titanium Gr 12 Pipes & Tubes Stcokists in UAE, Titanium Gr 12 Pipes & Tubes Exporters in UAE

Titanium Grade 12 Pipe and Tube Specification

Specifications : ASTM B861, B862, B338 / ASME SB861, SB862, SB338
Standard : ASTM, ASME and API
Size : 15mm NB to 150mm NB (1/2″ to 6″), 7″ (193.7mm OD to 20″ 508mm OD)
Outer Diameter : 1.250″ – 6.000″ (30-150mm)
Well Thickness : 0.095″ – 1.000″ (.2.5-25mm)
Length : Single Random, Double Random & Required Length
Schedule : SCH 10, SCH20, SCH30, SCH40, STD, SCH60, XS, SCH80, SCH120, SCH140, SCH160, XXS
Types : Seamless / ERW / Welded / EFW / Fabricated / CDW
Form : Round Pipes/Tubes, Square Pipes/Tubes, Rectangular Pipe/Tubes, Coiled Tubes, “U” Shape, Pan Cake Coils, Hydraulic Tubes
End : Plain End, Beveled End, Treaded

Titanium Gr 12 Pipes & Tubes Manufacturers in Dubai, Titanium Gr 12 Pipes & Tubes Suppliers in Dubai, Titanium Gr 12 Pipes & Tubes Stcokists in Dubai, Titanium Gr 12 Pipes & Tubes Exporters in Dubai

Grade	C	N	O	H	Ti	Fe
Titanium Grade 12	0.08 max	.03 max	.25 max	.015 max	Bal	0.30 max

Element	Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
Titanium Grade 12	4.43 g/cm3	1632 °C (2970 °F)	Psi – 138000 , MPa – 950	Psi – 128000 , MPa – 880	14 %

STANDARD	WERKSTOFF NR.	UNS
Titanium Grade 12	3.7105	R53400

Hardness, Brinell	256	256	Estimated from Rockwell C
Hardness, Knoop	278	278	Estimated from Rockwell C.
Hardness, Rockwell C	24	24	annealed
Hardness, Vickers	280	280	Estimated from Brinell.
Tensile Strength, Ultimate	89900 MPa	620 psi
Tensile Strength, Yield	500 MPa	72500 psi
Elongation at Break	15 %	15 %
Modulus of Elasticity	100 Gpa	14500 ksi
Compressive Yield Strength	105 GPa	100000 ksi	In Tension
Notched Tensile Strength	790 MPa	115000 psi ksi
Poisson's Ratio	0.3	0.3
Charpy Impact	86 J	63.4 ft-lb	V-notch
Shear Modulus	44 GPa	6380 ksi
Fatigue Strength	280 MPa	40600 psi	50,000 cycles. Kt (stress concentration factor) = 1.8